Products
Hastelloy B-2 Bars & Rods
| Alloy Name | Hastelloy B-2 Alloy |
| UNS | N10665 |
| W.Nr./EN | 2.4617 |
| Standard | ASTM B335 / ASME SB335 |
| Type | Round Bars, Square Bars, Hexagonal Bars (Rods) |
| Condition | Solution Annealed (Heat Treated) |
| Surface | Solution Annealed (Heat Treated) |
| Nickel (Ni) | 61.0% min |
| Molybdenum (Mo) | 26.0 – 30.0% |
| Iron (Fe) | ≤ 2.0% |
| Chromium (Cr) | ≤ 1.0% |
| Cobalt (Co) | ≤ 1.0% |
| Manganese (Mn) | ≤ 1.0% |
| Carbon (C) | ≤ 0.02% |
| Silicon (Si) | ≤ 0.1% |
| Phosphorus (P) | ≤ 0.04% |
| Sulfur (S) | ≤ 0.03% |
| Density | g/cm³ | 9.22 |
| Melting Range | lb/cu in | 0.333 |
| °C | 1345 – 1390 | |
| °F | 2450 – 2530 | |
| Modulus of Elasticity | GPa | 217 (20°C) |
| ksi | 31.5 x 10³ (70°F) | |
| Thermal Expansion (20–538°C) | µm/m·°C | 11.2 |
| Thermal Conductivity (100°C) | W/m·K | 10.5 |
| Temperature | Yield strength | Tensile strength | Elongation | |||
| Rp 0.2 | Rm | A | ||||
| °C | °F | MPa | ksi | MPa | ksi | % |
| 20 | 68 | ≥ 310 | ≥ 45 | ≥ 793 | ≥ 793 | ≥ 40 |
Applications of Hastelloy® B-2 Alloy Bars & Rods
Chemical & Acid Processing
Used in reaction vessels, heat exchangers and valve parts. Excellent resistance to hydrochloric acid, sulfuric acid and reducing media ensures reliable performance in highly corrosive acid environments.
Petrochemical Engineering
Applied in pump shafts, fasteners and reactor components. Resistant to stress corrosion cracking and pitting, maintaining stability in high-temperature and corrosive refining conditions.
Pickling & Surface Treatment
Used for heating rods, fixtures and conveying parts. Superior corrosion resistance to hot acidic solutions extends service life in metal pickling systems.
Pharmaceutical Machinery
Suitable for reactor shafts, mixing rods and precision parts. Provides stable corrosion resistance in corrosive production media and meets hygienic manufacturing requirements.
Waste & Environmental Treatment
Used in acidic wastewater treatment and flue gas desulfurization components. Withstands harsh corrosive media to ensure stable operation in environmental protection equipment.
| Alloy Name | Hastelloy B-2 Alloy |
| UNS | N10665 |
| W.Nr./EN | 2.4617 |
| Standard | ASTM B335 / ASME SB335 |
| Type | Round Bars, Square Bars, Hexagonal Bars (Rods) |
| Condition | Solution Annealed (Heat Treated) |
| Surface | Solution Annealed (Heat Treated) |
| Nickel (Ni) | 61.0% min |
| Molybdenum (Mo) | 26.0 – 30.0% |
| Iron (Fe) | ≤ 2.0% |
| Chromium (Cr) | ≤ 1.0% |
| Cobalt (Co) | ≤ 1.0% |
| Manganese (Mn) | ≤ 1.0% |
| Carbon (C) | ≤ 0.02% |
| Silicon (Si) | ≤ 0.1% |
| Phosphorus (P) | ≤ 0.04% |
| Sulfur (S) | ≤ 0.03% |
| Density | g/cm³ | 9.22 |
| Melting Range | lb/cu in | 0.333 |
| °C | 1345 – 1390 | |
| °F | 2450 – 2530 | |
| Modulus of Elasticity | GPa | 217 (20°C) |
| ksi | 31.5 x 10³ (70°F) | |
| Thermal Expansion (20–538°C) | µm/m·°C | 11.2 |
| Thermal Conductivity (100°C) | W/m·K | 10.5 |
| Temperature | Yield strength | Tensile strength | Elongation | |||
| Rp 0.2 | Rm | A | ||||
| °C | °F | MPa | ksi | MPa | ksi | % |
| 20 | 68 | ≥ 310 | ≥ 45 | ≥ 793 | ≥ 793 | ≥ 40 |